Nylon (PA6)

Nylon Rods, Bushes, Profiles, and Machinery parts are characterized by a combination of high strength, toughness and abrasion resistances. Our products replace metals in various engineering applications as they are manufactured by Extrusion Technique and therefore they have excellent physical and mechanical properties, some of the outstanding characteristics are as follows:

Reduction in weight
Self-lubricating economy
Shock resistance
Improved dimensional stability
Vibration damping performance
High wear and abrasion resistance
Noise reduction
High service temperature
High tensile and compressive Strengths Machining

APPLICATIONS

ENGINEERING	Gears, cams, sprockets, bushes, bearings, gaskets, pulleys, liners.
TEXTILE	Loom pivot bearings, gears for loom and knitting machines, shuttles, rollers, cams, and cam followers.
METAL	Bearings, bearing cages, slipper pads, gears, bushes, wear strips, rollers, eccentric rollers, wobble box inserts.
MATERIAL HANDLING EQUIPMENTS	Cranes/Fork lifts/Conveyors, Ropeways
AUTOMOBILE	Wear rings, pads, swivel bushes, throttle linkages, bushes, shackle pin bushes
PAPER / SUGAR MILLS	Gears, bushes, pulleys, rollers bearings
BOTTLING & FOOD PROCESSING	Star wheels, scrolls, guides, cams, cam followers, rollers, timing screws
RAILWAYS	Bushes, wear plates
CHEMICAL	Balls, gaskets, liners, nuts & bolts
MARINE	Bushes, gears, rings, trunnion bearings, rollers and roller bearings stern

PROPERTIES OF NYLON RODS

Property	Condition	Test Method	Unit	Value
Specific Gravity	Dry	ASTM D792	-	1.12.1.14
Water absorption 24 hrs.	Dry	ASTM D 570	%	3.5
Saturation	Dry	ASTM D570	%	8.5 - 10.0

MECHANICAL PROPERTIES

Property	Condition	Test Method	Unit	Value
Tensile Strength	Dry	ASTM D638	Kg/cm2	800
Tensile Strength	Moist*	ASTM D638	Kg/cm2	500
Elongation at break	Dry	ASTM D638	%	30-100
Elongation at break	Moist*	ASTM D638	%	200-300
Modulus of elasticity	Dry	ASTM D638	Kg/cm2	23000
Modulus of elasticity	Moist*	ASTM D638	Kg/cm2	6000-13000
Flexural Strength	Dry	ASTM D	Kg/cm2	1100-1150
Notched Impact Strength Izod	-	ASTM D	Cm - Kg/cm2	3-6
Shore Hardness	Dry	DIN 53505	Scale D	65
Coefficient of friction (nylon / steel) no lubrication	-	-	-	0.3-0.4
Initial lubrication	-	-	-	0.05 - 0.1

THERMAL PROPERTIES

Property	Condition	Test Method	Unit	Value
Melting Point	Dry	ASTM D569	0C	210 - 216
Flammability	Dry	ASTM D635	-	Self. Ext.
Heat Distortion Temperature 66psi	Dry	ASTM D648	0C	145 - 160
Heat Distortion Temperature 265psi	Dry	ASTM D648	0C	65
Maximum service temperature continuous	Dry	-	0C	90
Intermittent	Dry	-	0C	130
Coefficient of thermal expansion	Dry	ASTM D696	106 / 0C	100 - 120

ELECTRICAL PROPERTIES

Property	Condition	Test Method	Unit	Value
Dielectric Strength	Dry	ASTM D149	V/Mill	400

NYLON EXTRUDED SHEETS

THICKNESS	WIDTH	LENGTH
10mm to 100mm	700mm	1200mm long
10mm to 100mm	1000mm	2000mm long

Nylon Mos2

Extruded Nylon 6 with controlled quantity of MoS2 (Molybdenum Di Sulphide) to enhance sliding (wear) and self - lubricating properties. Better outdoor performance is achieved (UV radiation).

Oilon Rods (PA 6C + blended lubricant) Green

A complex blended oil lubrication system, uniformly distributed throughout the product guarantees constant performance over the whole service life of this exceptional oil-loaded nylon. Excellent sliding frictional properties, abrasion resistance and stick/slip performance make this product a first choice for unlubricated moving parts

First authentic lubricated nylon
Improved wear and abrasion resistance
Improved PV characteristics
Improved coefficient of friction and stick/slip characteristics
Consistent wear performance throughout product life
Reduced water absorption
Excellent mechanical, thermal and chemical resistance properties
Good dimensional stability
FDA compliant for direct food contact applications
Blended liquid lubricant system

Colours:- Black - Blue – Green